Physicochemical characteristics and discolouration potentials of Pulpine mineral® and Pulpine NE®

Autores/as

DOI:

https://doi.org/10.5195/d3000.2024.533

Palabras clave:

MTA, Pulpine NE, Pulpine mineral, Radiopacity, Solubility, Crown discoloration

Resumen

ABSTRACT

Aim: To compare the physicochemical properties (solubility, pH, radiopacity and crown discoloration) of Pulpine mineral (PMIN) and Pulpine NE (PNE) with the conventional material, mineral trioxide aggregate (MTA).

Methodology: Specimens of the tested materials were prepared according to the manufacturers instructions using split Teflon ring molds. Solubility was evaluated by the percentage of material mass loss over 24 h and one week. The alkalinity was measured after each evaluation period using a pH meter. Other specimens were digitally radiographed on a size 2 sensor plate along with an aluminum step wedge to analyze the radiopacity by the Image J software. Finally, crown discoloration was assessed after applying the tested materials in the pulp chamber of sound human premolars using spectrophotometer. All data were statistically analyzed.

Results: Compared to MTA, both materials had significantly higher solubility and lower radiopacity (P<0.05). The alkalinity of PMIN was higher than that of MTA and PNE. Unlike PMIN, PNE and MTA caused crown discoloration.

Conclusions: PMIN exhibits promising results related to high alkalinity and adequate color stability but it needs modifications for radiopacity and solubility.

Biografía del autor/a

Ashraf Abu-Seida, Cairo University

 Professor of Surgery, Anesthesiology & Radiology at Faculty of Veterinary Medicine, Cairo University

Ahmed Hashem, Ain Shams University (Endodontics Department)

professor and  head of Endodontic department till 4-2023 , Ain Shams University

Citas

References

Mesenchymal stem cells promote hard-tissue repair after direct pulp capping. Obeid M, Saber Sel D, Ismael Ael D, Hassanien E. J Endod. 2013 May;39(5):626-31. PMID: 23611380.

Outcome of pulpotomy in permanent teeth with irreversible pulpitis: a systematic review and meta-analysis. Ather A, Patel B, Gelfond JAL, Ruparel NB. Sci Rep. 2022 Nov 16;12(1):19664. PMID: 36385132.

Physicochemical Properties of a Bioceramic Repair Material - BioMTA. Coaguila-Llerena H, Ochoa-Rodriguez VM, Castro-Núñez GM, Faria G, Guerreiro-Tanomaru JM, Tanomaru-Filho M. Braz Dent J. 2020 Sep-Oct;31(5):511-515. PMID: 33146335.

https://hoffmann-dental.com/produkte/?lang=en.

Histopathological and immunohistochemical profiles of pulp tissues in immature dogs' teeth to two recently introduced pulpotomy materials. Mohamed M, Hashem AAR, Obeid MF, Abu-Seida A. Clin Oral Investig. 2023 Jun;27(6):3095-3103. PMID: 36781475.

Evaluation of antibacterial activity of propolis on regenerative potential of necrotic immature permanent teeth in dogs. El-Tayeb MM, Abu-Seida AM, El Ashry SH, El-Hady SA. BMC Oral Health. 2019 Aug 6;19(1):174. PMID: 31387578.

Biological evaluation of hesperidin for direct pulp capping in dogs' teeth. Abo El-Mal EO, Abu-Seida AM, El Ashry SH. Int J Exp Pathol. 2021 Feb;102(1):32-44. PMID: 33405328.

Hydroxyapatite applied as direct pulp capping medicine substitutes for osteodentin. Hayashi Y, Imai M, Yanagiguchi K, Viloria IL, Ikeda T. J Endod. 1999 Apr;25(4):225-9. PMID: 10425944.

Evaluation of the tissue reaction to fast endodontic cement (CER) and Angelus MTA. Gomes-Filho JE, Rodrigues G, Watanabe S, Estrada Bernabé PF, Lodi CS, Gomes AC, Faria MD, Domingos Dos Santos A, Silos Moraes JC. J Endod. 2009 Oct;35(10):1377-80. PMID: 19801233.

Physiochemical properties of experimental nano-hybrid MTA. Akhavan Zanjani V, Tabari K, Sheikh-Al-Eslamian SM, Abrandabadi AN. J Med Life. 2017 Jul-Sep;10(3):182-187. PMID: 29075348.

Marginal adaptation, solubility and biocompatibility of TheraCal LC compared with MTA-angelus and biodentine as a furcation perforation repair material. Alazrag MA, Abu-Seida AM, El-Batouty KM, El Ashry SH. BMC Oral Health. 2020 Oct 29;20(1):298. PMID: 33121465.

ANSI/ADA (2000) Specification no 57 Endodontic sealing material. Chicago, USA: ADA Publishing.

Densitometric measurement of radiopacity of Gutta-percha cones and root dentin. Katz A, Kaffe I, Littner M, Tagger M, Tamse A. J Endod. 1990 May;16(5):211-3. PMID: 2074412.

Bioceramic materials in endodontics. Endodontic topics. Wang Z. 2015;32:3-0.

A Review of Tooth Discoloration after Regenerative Endodontic Therapy. Kahler B, Rossi-Fedele G. J Endod. 2016;42(4):563-569. PMID: 26852148.

Solubility and dimensional change after setting of root canal sealers: a proposal for smaller dimensions of test samples. Carvalho-Junior JR, Correr-Sobrinho L, Correr AB, Sinhoreti MA, Consani S, Sousa-Neto MD. J Endod. 2007;33(9):1110-1116. PMID: 17931945.

Effects of the addition of nanoparticulate calcium carbonate on setting time, dimensional change, compressive strength, solubility and pH of MTA. Bernardi A, Bortoluzzi EA, Felippe WT, Felippe MC, Wan WS, Teixeira CS. Int Endod J. 2017;50(1):97-105. PMID: 26659859.

A laboratory evaluation of cell viability, radiopacity and tooth discoloration induced by regenerative endodontic materials. Oliveira LV, da Silva GR, Souza GL, Magalhães TEA, Barbosa GLR, Turrioni AP. Int Endod J. 2020; 53:1140-1152. PMID: 32299123.

Color stability of teeth restored with biodentine: A 6-month in vitro study. Vallés M, Roig M, Duran-Sindreu F, Martínez S, Mercadé M. J Endod. 2015; 41:1157-1160. PMID: 25937179.

Spectrophotometric Analysis of Coronal Tooth Discoloration Induced by Tricalcium Silicate Cements in the Presence of Blood. Chen SJ, Karabucak B, Steffen JJ, Yu YH, Kohli MR. J Endod. 2020;46(12):1913–9. PMID : 32949559.

Solubility of Root-end-Filling Materials: A Comparative Study. Poggio C, Lombardini M, Alessandro C, Simonetta R. J Endod. 2007;33(9):1094–7. PMID: 17931941.

Changes in the surface of four calcium silicate-containing endodontic materials and an epoxy resin-based sealer after a solubility test. Borges RP, Sousa-Neto MD, Versiani MA, Rached-Júnior FA, De-Deus G, Miranda CES. Int Endod J. 2012; 45:419-428. PMID: 22150403.

Nucleophilic effects on the deprotonation of phenol radical cations. Chem Phys Lett. 2001; 337:335-340.

A comparative study of the physicochemical properties of hesperidin, MTA-Angelus and calcium hydroxide as pulp capping materials. Abo El-Mal EO, Abu-Seida AM, El Ashry SH. Saudi Dent J. 2019; 31: 219-227. PMID: 30983832.

Antimicrobial Activity and pH of Calcium Hydroxide and Zinc Oxide Nanoparticles Intracanal Medication and Association with Chlorhexidine. Aguiar AS, Guerreiro-Tanomaru JM, Faria G, Leonardo RT, Tanomaru-Filho M. J Contemp Dent Pract. 2015; 16:624-629. PMID: 26423497.

Physical evaluation of a new pulp capping material developed from Portland cement. Negm A, Hassanien E, Abu-Seida AM, Nagy M. J Clin Exper Dent. 2016; 8, e278–e283. PMID: 27398178.

Influence of powder-to-water ratio on radiopacity, setting time, pH, calcium ion release and micro-CT volumetric solubility of white mineral trioxide aggregate. Cavenago BC, Pereira TC, Duarte MAH. Int Endod J. 2014; 47:120-126. PMID: 23647286.

Radiopacity of Portland cement associated with different radiopacifying agents. Húngaro Duarte MA, de Oliveira El Kadre GD ar, Vivan RR, Guerreiro Tanomaru JM, Filho MT, de Moraes IG. J Endod. 2009; 35:737-740. PMID: 19410095.

Radiopacity of root filling materials using digital radiography. Carvalho-Junior JR, Correr-Sobrinho L, Correr AB, Sinhoreti MAC, Consani S, Sousa-Neto MD. Int Endod J. 2007; 40 :514-520. PMID: 17511790.

Mineral trioxide aggregate enriched with iron disulfide nanostructures: an evaluation of their physical and biological properties. Argueta-Figueroa L, Delgado-García JJ, García-Contreras R. Eur J Oral Sci. 2018; 126:234-243. PMID: 29442393.

Comparison of the physical and mechanical properties of MTA and portland cement. Islam I, Kheng Chng H, Jin Yap AU. J Endod. 2006; 32:193-197. PMID: 16500224.

Effect of zirconium oxide and zinc oxide nanoparticles on physicochemical properties and antibiofilm activity of a calcium silicate-based material. Guerreiro-Tanomaru JM, Trindade-Junior A, Costa BC. Sci World J. 2014: Article ID 975213. PMID: 25431798.

Color stability of white mineral trioxide aggregate. Vallés M, Mercadé M, Duran-Sindreu F, Bourdelande JL, Roig M. Clin Oral Investig. 2013; 17:1155-1159. PMID: 22814761.

Does Modification of Amalgomer with Propolis Alter Its Physicomechanical Properties? An In Vitro Study. Abdallah Abdallah RM, Abdelghany AM, Aref NS. Int J Biomater. 2020;2020:3180879. PMID: 32454828.

Whitening effect and morphological evaluation of hydroxyapatite materials. Dabanoglu A, Wood C, García-Godoy F, Kunzelmann KH. Am J Dent. 2009; 22:23-29. PMID: 19281109.

Publicado

2024-05-06

Número

Sección

Mechanisms of Oral Disease